BITUMENS MASTICS AND PRIMER

vadim — Wed, 17 Oct 2018 09:09:55 +0000

BITUMEN PRIMER MATIZOL

Bitumen primer is a solution of petroleum bitumen in organic solvents with synthetic modifying additives and siccatives. After drying, it forms a hard glossy black coating with high resistance to atmospheric influences. It has a high penetrating power and a short drying time.

Application:

for the preparation (priming) of surfaces (concrete slab, cement-sand screed, etc.) before laying surfaced and self-adhesive roofing and waterproofing materials

Bitumen primer is recommended to be applied to the surface to be treated with brushes or brushes. With this application, the primer is rubbed into the surface, saturates and binds it, ensuring a strong adhesion of the waterproofing coating to the base.

BITUMEN MASTIC FOR ROOF MATIZOL

Mastic consists of oil bitumen modified by artificial polymers, mineral fillers and organic solvent. After drying, material forms highly strong and elastic covering, highly resistant to temperature changes, considerably increasing the service life of the protected surfaces.

Application areas:

entire roof waterproofing including details and parapets
waterproofing of engineering structures (basements, footings, piles and other building elements buried under ground likely to be in contact with damp environment)
weatherproofing and anti-corrosion treatment of metal surfaces including pipelines and car bodies

Mastic should be applied to prepared surface clear of any debris and surplus materials, mastic can be applied by using stiff paint brush, filling knife or by pouring and leveling. Single layer thickness should not exceed 1.5 mm, each subsequent layer must be applied after previous layer is completely dry. It is highly recommended to apply minimum of 2 layers, to achieve durable waterproofing.

WATERPROOFING MASTIC MATIZOL

Mastic is a waterproofing solution combining elasticity, durability and economy. Material contains polymer additives, mineral fillers and solvents.

Application areas:

waterproofing of concrete or wood surfaces
protection of engineering structures (basements, piles and other elements of construction)

Mastic should be applied to prepared surfaces clear of any debris and surplus materials, by using stiff paint brush, filling knife or by pouring and leveling.

Ruberoid

vadim — Wed, 17 Oct 2018 08:57:41 +0000

RUBEROID

Ruberoid – is a a roll-fed roofing, waterproofing material. Produced by placing a bitumen binder on roofing paper. The protective dressing compound (talc, etc.) is applied to both sides.

Application:

ruberoid RKPO-350 – underlay
ruberoid RKK-350 – top layer

Asphalt paper – is a roofing paper impregnated with oil asphalts.

Application areas:

underlay
vapor and waterproofing of roof and other structures

	RUBEROID RKPO-350	RUBEROID RKK-350	ASPHALT PAPER
Length, m	15	10	20
Width, m	1	1	1
Elongation L/T, %	–	2/2	–
Tensile strength L/T, N/50 mm	425/300	450/300	150/100
Flow resistance at elevated temperature, °C	≤+80	≤+80	≤+80
Cold flexibility, °С	≤+5	≤+5	≤+5
Weight, kg	15	27	14

	Length, m	Width, m	Elongation L/T, %	Tensile strength L/T, N/50 mm	Flow resistance at elevated temperature, °C	Cold flexibility, °С	Weight, kg
RUBEROID RKPO-350	15	1	–	425/300	≤+80	≤+5	15
RUBEROID RKK-350	10	1	2/2	450/300	≤+80	≤+5	27
ASPHALT PAPER	20	1	–	150/100	≤+80	≤+5	14

PVC membranes

vadim — Tue, 16 Oct 2018 09:38:52 +0000

PVC membranes

Buildings of all types require a durable roof. The roof should have a long service life without substantial repair.

Use of long-lasting roofing systems made of synthetic membranes is a modern solution, which combines reliability and rapid installation. DANOPOL PVC membranes are high-tech materials, designed for long-term waterproofing of buildings and structures. They are contemporary, reliable and durable waterproofing materials produced using co-extrusion technology – currently the best on the market.

DANOPOL HS 1.5

Smooth PVC membrane reinforced with polyester. Installed at temperatures that are at least -20 °C.

	DANOPOL HS 1.5
Biezums, mm	1.5
Stiepes stiprība L/T, N/50 mm	1100 / 1000
Pagarinājums L/T, %	≥20
Elastība, ºС	-30
Ruļļa izmērs, m	1,80 x 15,00 m
Virsmas tonis	RAL 7047

	Biezums, mm	Stiepes stiprība L/T, N/50 mm	Pagarinājums L/T, %	Elastība, ºС	Apjoms uz paliktņa, m2
LOGICROOF V-RP T	1.2 \| 1.5 \| 1.8. \| 2.0	1100 / 900	≥18	-30	945 \| 756 \| 567 \| 567

DANOPOL HS 1.2

Smooth PVC membrane reinforced with polyester. Installed at temperatures that are at least -20 °C.

	Biezums, mm	Stiepes stiprība L/T, N/50 mm	Pagarinājums L/T, %	Elastība, ºС	Apjoms uz paliktņa, m2
LOGICROOF V-RP	1.2 \| 1.5 \| 1.8. \| 2.0	1100 / 900	≥18	-35	945 \| 756 \| 567 \| 567

	DANOPOL HS 1.2
Biezums, mm	1.2
Stiepes stiprība L/T, N/50 mm	1000/ 1000
Pagarinājums L/T, %	≥15
Elastība, ºС	-30
Ruļļa izmērs, m	1,80 x 20,00
Virsmas tonis	RAL 7047

Bitumen membranes

vadim — Tue, 16 Oct 2018 08:02:32 +0000

Bitumen membranes

The most widespread materials for the creation of the waterproofing layer are the polymer-bitumen roll-fed membranes. This is due to a relative simplicity of installation, popularity of the technology, durability of the material and stability of the factory-set technical parameters.

Polymer-bitumen membranes are commonly used for waterproofing of foundations, engineering structures, roads, bridge decks and flat roofs. These materials could also be used as an underlay for pitched roofs and as a vapor barrier.

The waterproofing membrane not only protects the internal premises from water penetrating inside, reducing their operating ability, disturbing the process equipment operation and worsening the microclimatic conditions indoors, but it also prevents the destruction of the foundation and supporting structures. Therefore, the correct selection and installation of the waterproofing membrane also ensure the durability of the whole facility.

One layer modified bitumen materials

	Ruļļa garums/platums (m)	Pamatnes veids	Biezums (mm)	Svars (kg/m²)	Elastība zemās temperatūrās (°С)	Siltumizturība (°С)	Pārraušanas spēks G/Š (N/50mm)	Pārraušanas spēks ar naglu G/Š (N)	Īpašais pagarinājums G/Š (%)
MIDA FIX TOP PV S5	7.5×1	Poliesters	5.2	6.3	≤-25	≥+100	1000/800	300/300	40/40

Top layer modified bitumen materials

	Ruļļa garums/platums (m)	Pamatnes veids	Biezums (mm)	Svars (kg/m²)	Elastība zemās temperatūrās (°С)	Siltumizturība (°С)	Pārraušanas spēks G/Š (N/50mm)	Pārraušanas spēks ar naglu G/Š (N)	Īpašais pagarinājums G/Š (%)
MIDA TECHNOELAST K-PS 170/5000	8×1	Poliesters	4.0	5.0	≤-25	≥+100	700/500	250/250	50/50
MIDA TECHNOELAST PV S5b	5×1	Poliesters	5.0	6.3	≤-25	≥+100	1000/900	400/400	40/40
MIDA TECHNOELAST PV S4b	10×1	Poliesters	4.2	5.2	≤-25	≥+100	900/650	300/300	40/40
MIDA UNIFLEKS EKP 5.0	10×1	Poliesters	4.0	5.0	≤-20	≥+95	850/650	250/250	40/40
MIDA UNIFLEKS EKP 5.0 balts	10×1	Poliesters	4.0	5.0	≤-20	≥+90	850/650	250/250	40/40
MIDA BALT PV S4b	10×1	Poliesters	4.2	5.2	≤-20	≥+95	900/650	300/300	40/40
MIDA UNIFLEKS PV S4b	10×1	Poliesters	4.0	5.0	≤-15	≥+100	850/650	250/250	40/40
MIDA BIPOL STANDART EKP	10×1	Poliesters	3.5	4.5	≤-15	≥+90	600/500	230/230	40/40
MIDA BIPOL EKP 4.0	10×1	Poliesters	3.0	4.0	≤-15	≥+90	600/500	230/230	40/40
BIKROELAST EKP 4.0	10×1	Poliesters	3.2	4.0	≤-10	≥+85	600/500	230/230	40/40

Underlay modified bitumen materials

	Ruļļa garums/platums (m)	Pamatnes veids	Biezums (mm)	Svars (kg/m²)	Elastība zemās temperatūrās (°С)	Siltumizturība (°С)	Pārraušanas spēks G/Š (N/50mm)	Pārraušanas spēks ar naglu G/Š (N)	Īpašais pagarinājums G/Š (%)
MIDA TECHNOELAST K-MS 170/4000	10×1	Poliesters	3.0	4.0	≤-25	≥+100	700/500	250/250	50/50
MIDA TECHNOELAST PV S5s	5×1	Poliesters	5.0	6.1	≤-25	≥+100	1000/900	400/400	40/40
MIDA TECHNOELAST PV S4s	10×1	Poliesters	4.0	5.0	≤-25	≥+100	900/650	300/300	40/40
MIDA UNIFLEKS EPP 4.0	10×1	Poliesters	3.0	4.0	≤-20	≥+95	800/600	200/200	40/40
MIDA BALT PV S3s	10×1	Poliesters	3.0	4.0	≤-20	≥+95	800/600	250/250	40/40
MIDA UNIFLEKS PV S3s	10×1	Poliesters	3.0	4.0	≤-15	≥+95	800/600	200/200	40/40
MIDA BIPOL STANDART EPP	10×1	Poliesters	2.5	3.5	≤-15	≥+85	600/500	230/230	40/40
MIDA BIPOL EPP 3.0	15×1	Poliesters	2.3	3.0	≤-15	≥+90	600/500	230/230	40/40
MIDA BIKROELAST EPP 4.0	15×1	Poliesters	3.0	4.0	≤-10	≥+85	600/500	200/200	40/40
BIKROELAST EPP 3.0	15×1	Poliesters	2.3	3.0	≤-10	≥+85	600/500	200/200	50/50

Self-adhesive materials

	Ruļļa garums/platums (m)	Pamatnes veids	Biezums (mm)	Svars (kg/m²)	Elastība zemās temperatūrās (°С)	Siltumizturība (°С)	Pārraušanas spēks G/Š (N/50mm)	Pārraušanas spēks ar naglu G/Š (N)	Īpašais pagarinājums G/Š (%)
MIDA SELF SA P 2mm	20×1	Poliesters	2.0	2.3	≤-20	≥+90	450/350	200/200	30/30
MIDA SELF PRO	15×1	Poliesters	1.5	1.8	≤-15	≥+90	400/350	200/200	30/30

Waterproofing – Ilguciems

BITUMENS MASTICS AND PRIMER

BITUMEN PRIMER MATIZOL

BITUMEN MASTIC FOR ROOF MATIZOL

WATERPROOFING MASTIC MATIZOL

Ruberoid

RUBEROID

RUBEROID RKPO-350

RUBEROID RKK-350

ASPHALT PAPER

RUBEROID RKPO-350

RUBEROID RKK-350

ASPHALT PAPER

PVC membranes

PVC membranes

DANOPOL HS 1.5

DANOPOL HS 1.5

DANOPOL HS 1.2

LOGICROOF V-RP

DANOPOL HS 1.2

Bitumen membranes

Bitumen membranes

One layer modified bitumen materials

Top layer modified bitumen materials

Underlay modified bitumen materials

Self-adhesive materials